N10003 Nickel vs. ACI-ASTM CN7MS Steel
N10003 nickel belongs to the nickel alloys classification, while ACI-ASTM CN7MS steel belongs to the iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N10003 nickel and the bottom bar is ACI-ASTM CN7MS steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 42 | |
| 39 |
| Fatigue Strength, MPa | 260 | |
| 200 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 1040 |
| Melting Completion (Liquidus), °C | 1520 | |
| 1400 |
| Melting Onset (Solidus), °C | 1460 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Conductivity, W/m-K | 12 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 28 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 5.1 |
| Embodied Energy, MJ/kg | 180 | |
| 71 |
| Embodied Water, L/kg | 270 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 260 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 19 |
| Strength to Weight: Bending, points | 21 | |
| 19 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 3.2 |
| Thermal Shock Resistance, points | 21 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.5 | |
| 0 |
| Boron (B), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0.040 to 0.080 | |
| 0 to 0.070 |
| Chromium (Cr), % | 6.0 to 8.0 | |
| 18 to 20 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 1.5 to 2.0 |
| Iron (Fe), % | 0 to 5.0 | |
| 45.4 to 53.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 15 to 18 | |
| 2.5 to 3.0 |
| Nickel (Ni), % | 64.8 to 79 | |
| 22 to 25 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 2.5 to 3.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 to 0.5 | |
| 0 |
| Vanadium (V), % | 0 to 0.5 | |
| 0 |