N10003 Nickel vs. EN 2.4665 Nickel
Both N10003 nickel and EN 2.4665 nickel are nickel alloys. They have 67% of their average alloy composition in common.
For each property being compared, the top bar is N10003 nickel and the bottom bar is EN 2.4665 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Elongation at Break, % | 42 | |
| 34 |
| Fatigue Strength, MPa | 260 | |
| 220 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 81 |
| Shear Strength, MPa | 540 | |
| 520 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 790 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 990 |
| Melting Completion (Liquidus), °C | 1520 | |
| 1460 |
| Melting Onset (Solidus), °C | 1460 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 450 |
| Thermal Conductivity, W/m-K | 12 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.4 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 55 |
| Density, g/cm3 | 8.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 9.2 |
| Embodied Energy, MJ/kg | 180 | |
| 130 |
| Embodied Water, L/kg | 270 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 260 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 220 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 26 |
| Strength to Weight: Bending, points | 21 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 3.2 |
| Thermal Shock Resistance, points | 21 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.5 | |
| 0 to 0.5 |
| Boron (B), % | 0 to 0.010 | |
| 0 to 0.010 |
| Carbon (C), % | 0.040 to 0.080 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 6.0 to 8.0 | |
| 20.5 to 23 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0.5 to 2.5 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 5.0 | |
| 17 to 20 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 15 to 18 | |
| 8.0 to 10 |
| Nickel (Ni), % | 64.8 to 79 | |
| 40.3 to 53.8 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 to 0.5 | |
| 0.2 to 1.0 |
| Vanadium (V), % | 0 to 0.5 | |
| 0 |