N10003 Nickel vs. Solder Alloy 122

N10003 nickel belongs to the nickel alloys classification, while solder alloy 122 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N10003 nickel and the bottom bar is solder alloy 122.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
20
Elongation at Break, % 42
30
Poisson's Ratio 0.3
0.43
Shear Modulus, GPa 80
6.9
Tensile Strength: Ultimate (UTS), MPa 780
30

Thermal Properties

Latent Heat of Fusion, J/g 320
27
Melting Completion (Liquidus), °C 1520
300
Melting Onset (Solidus), °C 1460
270
Specific Heat Capacity, J/kg-K 420
140
Thermal Conductivity, W/m-K 12
25
Thermal Expansion, µm/m-K 13
28

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
7.3

Otherwise Unclassified Properties

Base Metal Price, % relative 70
75
Density, g/cm3 8.9
11
Embodied Carbon, kg CO2/kg material 13
5.0
Embodied Energy, MJ/kg 180
84
Embodied Water, L/kg 270
540

Common Calculations

Stiffness to Weight: Axial, points 13
1.0
Stiffness to Weight: Bending, points 22
8.2
Strength to Weight: Axial, points 24
0.77
Strength to Weight: Bending, points 21
2.0
Thermal Diffusivity, mm2/s 3.1
17
Thermal Shock Resistance, points 21
3.9

Alloy Composition

Aluminum (Al), % 0 to 0.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Boron (B), % 0 to 0.010
0
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0.040 to 0.080
0
Chromium (Cr), % 6.0 to 8.0
0
Cobalt (Co), % 0 to 0.2
0
Copper (Cu), % 0 to 0.35
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 5.0
0 to 0.020
Lead (Pb), % 0
88.4 to 90.5
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 15 to 18
0
Nickel (Ni), % 64.8 to 79
0 to 0.010
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
9.5 to 10.5
Tungsten (W), % 0 to 0.5
0
Vanadium (V), % 0 to 0.5
0
Zinc (Zn), % 0
0 to 0.0010