N10629 Nickel vs. EN 1.1152 Steel
N10629 nickel belongs to the nickel alloys classification, while EN 1.1152 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is N10629 nickel and the bottom bar is EN 1.1152 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 45 | |
| 12 to 22 |
| Fatigue Strength, MPa | 340 | |
| 190 to 300 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 73 |
| Shear Strength, MPa | 600 | |
| 290 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 400 to 550 |
| Tensile Strength: Yield (Proof), MPa | 400 | |
| 270 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 400 |
| Melting Completion (Liquidus), °C | 1610 | |
| 1460 |
| Melting Onset (Solidus), °C | 1560 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 1.8 |
| Density, g/cm3 | 9.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 1.4 |
| Embodied Energy, MJ/kg | 190 | |
| 18 |
| Embodied Water, L/kg | 270 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 41 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 200 to 530 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 22 | |
| 15 to 19 |
| Thermal Shock Resistance, points | 27 | |
| 13 to 17 |
Alloy Composition
| Aluminum (Al), % | 0.1 to 0.5 | |
| 0 |
| Carbon (C), % | 0 to 0.010 | |
| 0.18 to 0.22 |
| Chromium (Cr), % | 0.5 to 1.5 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.25 |
| Iron (Fe), % | 1.0 to 6.0 | |
| 98.6 to 99.52 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 26 to 30 | |
| 0 |
| Nickel (Ni), % | 65 to 72.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.050 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.025 |