N10629 Nickel vs. C26800 Brass
N10629 nickel belongs to the nickel alloys classification, while C26800 brass belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is N10629 nickel and the bottom bar is C26800 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Rockwell B Hardness | 88 | |
| 53 to 91 |
| Shear Modulus, GPa | 83 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 310 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 130 |
| Melting Completion (Liquidus), °C | 1610 | |
| 930 |
| Melting Onset (Solidus), °C | 1560 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Expansion, µm/m-K | 10 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 24 |
| Density, g/cm3 | 9.2 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 2.7 |
| Embodied Energy, MJ/kg | 190 | |
| 45 |
| Embodied Water, L/kg | 270 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 19 |
| Strength to Weight: Axial, points | 26 | |
| 11 to 22 |
| Strength to Weight: Bending, points | 22 | |
| 13 to 21 |
| Thermal Shock Resistance, points | 27 | |
| 10 to 22 |
Alloy Composition
| Aluminum (Al), % | 0.1 to 0.5 | |
| 0 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Chromium (Cr), % | 0.5 to 1.5 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 64 to 68.5 |
| Iron (Fe), % | 1.0 to 6.0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.15 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 |
| Molybdenum (Mo), % | 26 to 30 | |
| 0 |
| Nickel (Ni), % | 65 to 72.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.050 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 31 to 36 |
| Residuals, % | 0 | |
| 0 to 0.3 |