N10675 Nickel vs. SAE-AISI S5 Steel

N10675 nickel belongs to the nickel alloys classification, while SAE-AISI S5 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is N10675 nickel and the bottom bar is SAE-AISI S5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 85
72
Tensile Strength: Ultimate (UTS), MPa 860
680 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 11
42
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.2
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 80
3.1
Density, g/cm3 9.3
7.7
Embodied Carbon, kg CO2/kg material 16
2.1
Embodied Energy, MJ/kg 210
29
Embodied Water, L/kg 280
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
25
Strength to Weight: Axial, points 26
25 to 70
Strength to Weight: Bending, points 22
22 to 45
Thermal Diffusivity, mm2/s 3.1
11
Thermal Shock Resistance, points 26
23 to 65

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0.5 to 0.65
Chromium (Cr), % 1.0 to 3.0
0 to 0.5
Cobalt (Co), % 0 to 3.0
0
Copper (Cu), % 0 to 0.2
0 to 0.25
Iron (Fe), % 1.0 to 3.0
93.6 to 97
Manganese (Mn), % 0 to 3.0
0.6 to 1.0
Molybdenum (Mo), % 27 to 32
0.2 to 1.4
Nickel (Ni), % 51.3 to 71
0
Niobium (Nb), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.1
1.8 to 2.3
Sulfur (S), % 0 to 0.010
0 to 0.030
Tantalum (Ta), % 0 to 0.2
0
Titanium (Ti), % 0 to 0.2
0
Tungsten (W), % 0 to 3.0
0
Vanadium (V), % 0 to 0.2
0 to 0.35
Zinc (Zn), % 0 to 0.1
0