N12160 Nickel vs. SAE-AISI 1015 Steel
N12160 nickel belongs to the nickel alloys classification, while SAE-AISI 1015 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N12160 nickel and the bottom bar is SAE-AISI 1015 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 45 | |
| 20 to 32 |
| Fatigue Strength, MPa | 230 | |
| 170 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 73 |
| Shear Strength, MPa | 500 | |
| 260 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 390 to 440 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 210 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 360 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1060 | |
| 400 |
| Melting Completion (Liquidus), °C | 1330 | |
| 1470 |
| Melting Onset (Solidus), °C | 1280 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 90 | |
| 1.8 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 120 | |
| 18 |
| Embodied Water, L/kg | 400 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 260 | |
| 83 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 120 to 360 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 14 to 15 |
| Strength to Weight: Bending, points | 22 | |
| 15 to 16 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 14 |
| Thermal Shock Resistance, points | 19 | |
| 12 to 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.13 to 0.18 |
| Chromium (Cr), % | 26 to 30 | |
| 0 |
| Cobalt (Co), % | 27 to 33 | |
| 0 |
| Iron (Fe), % | 0 to 3.5 | |
| 99.13 to 99.57 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 25 to 44.4 | |
| 0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 2.4 to 3.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0.2 to 0.8 | |
| 0 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |