R04295 Alloy vs. Solder Alloy 601
Both R04295 alloy and solder alloy 601 are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is R04295 alloy and the bottom bar is solder alloy 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 31 |
| Elongation at Break, % | 22 | |
| 83 |
| Poisson's Ratio | 0.38 | |
| 0.41 |
| Shear Modulus, GPa | 37 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 410 | |
| 12 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 43 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 230 |
| Thermal Expansion, µm/m-K | 7.2 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 7.3 |
| Embodied Water, L/kg | 950 | |
| 1330 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.3 | |
| 2.3 |
| Stiffness to Weight: Bending, points | 17 | |
| 14 |
| Strength to Weight: Axial, points | 13 | |
| 0.45 |
| Strength to Weight: Bending, points | 14 | |
| 1.6 |
| Thermal Shock Resistance, points | 40 | |
| 1.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0 to 0.015 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Hafnium (Hf), % | 9.0 to 11 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Indium (In), % | 0 | |
| 51 to 52.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Niobium (Nb), % | 85.9 to 90.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.025 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tantalum (Ta), % | 0 to 0.5 | |
| 0 |
| Tin (Sn), % | 0 | |
| 47.5 to 48.5 |
| Titanium (Ti), % | 0.7 to 1.3 | |
| 0 |
| Tungsten (W), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Zirconium (Zr), % | 0 to 0.7 | |
| 0 |