R04295 Alloy vs. SAE-AISI 1017 Steel
R04295 alloy belongs to the otherwise unclassified metals classification, while SAE-AISI 1017 steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is R04295 alloy and the bottom bar is SAE-AISI 1017 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 22 | |
| 20 to 30 |
| Poisson's Ratio | 0.38 | |
| 0.29 |
| Shear Modulus, GPa | 37 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 410 | |
| 420 to 460 |
| Tensile Strength: Yield (Proof), MPa | 300 | |
| 220 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 260 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.2 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 7.9 |
| Embodied Water, L/kg | 950 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 | |
| 130 to 400 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 17 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 15 to 16 |
| Strength to Weight: Bending, points | 14 | |
| 16 to 17 |
| Thermal Shock Resistance, points | 40 | |
| 13 to 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.015 | |
| 0.15 to 0.2 |
| Hafnium (Hf), % | 9.0 to 11 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 | |
| 99.11 to 99.55 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Niobium (Nb), % | 85.9 to 90.3 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.025 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tantalum (Ta), % | 0 to 0.5 | |
| 0 |
| Titanium (Ti), % | 0.7 to 1.3 | |
| 0 |
| Tungsten (W), % | 0 to 0.5 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.7 | |
| 0 |