R05240 Alloy vs. 6008 Aluminum
R05240 alloy belongs to the otherwise unclassified metals classification, while 6008 aluminum belongs to the aluminum alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is R05240 alloy and the bottom bar is 6008 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 69 |
| Elongation at Break, % | 25 | |
| 9.1 to 17 |
| Poisson's Ratio | 0.36 | |
| 0.33 |
| Shear Modulus, GPa | 57 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 200 to 290 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 100 to 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 410 |
| Specific Heat Capacity, J/kg-K | 190 | |
| 900 |
| Thermal Expansion, µm/m-K | 6.8 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 14 | |
| 2.7 |
| Embodied Water, L/kg | 460 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 24 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 | |
| 76 to 360 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 13 | |
| 50 |
| Strength to Weight: Axial, points | 5.4 | |
| 21 to 29 |
| Strength to Weight: Bending, points | 6.8 | |
| 28 to 35 |
| Thermal Shock Resistance, points | 18 | |
| 9.0 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 96.5 to 99.1 |
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 0.7 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 35 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0.5 to 0.9 |
| Tantalum (Ta), % | 57.9 to 65 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 to 0.1 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |