R05240 Alloy vs. 6101 Aluminum

R05240 alloy belongs to the otherwise unclassified metals classification, while 6101 aluminum belongs to the aluminum alloys. There are 11 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is R05240 alloy and the bottom bar is 6101 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
68
Elongation at Break, % 25
10 to 25
Poisson's Ratio 0.36
0.33
Shear Modulus, GPa 57
26

Thermal Properties

Latent Heat of Fusion, J/g 210
400
Specific Heat Capacity, J/kg-K 190
900
Thermal Expansion, µm/m-K 6.8
23

Otherwise Unclassified Properties

Density, g/cm3 14
2.7
Embodied Water, L/kg 460
1190

Common Calculations

Stiffness to Weight: Axial, points 6.3
14
Stiffness to Weight: Bending, points 13
50

Alloy Composition

Aluminum (Al), % 0
97.6 to 99.4
Boron (B), % 0
0 to 0.060
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 0
0 to 0.030
Copper (Cu), % 0
0 to 0.1
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
0 to 0.5
Magnesium (Mg), % 0
0.35 to 0.8
Manganese (Mn), % 0
0 to 0.030
Molybdenum (Mo), % 0 to 0.020
0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Silicon (Si), % 0 to 0.0050
0.3 to 0.7
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.1