R05240 Alloy vs. ASTM B522 Class II
Both R05240 alloy and ASTM B522 class II are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R05240 alloy and the bottom bar is ASTM B522 class II.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 96 |
| Elongation at Break, % | 25 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.36 | |
| 0.41 |
| Shear Modulus, GPa | 57 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 280 to 490 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 120 to 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 77 |
| Specific Heat Capacity, J/kg-K | 190 | |
| 160 |
| Thermal Expansion, µm/m-K | 6.8 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 14 | |
| 17 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 4.4 to 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 | |
| 75 to 230 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 13 | |
| 8.9 |
| Strength to Weight: Axial, points | 5.4 | |
| 4.4 to 7.8 |
| Strength to Weight: Bending, points | 6.8 | |
| 5.5 to 8.0 |
| Thermal Shock Resistance, points | 18 | |
| 13 to 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Gold (Au), % | 0 | |
| 68.5 to 69.5 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 35 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.020 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 5.5 to 6.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Silver (Ag), % | 0 | |
| 24.5 to 25.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tantalum (Ta), % | 57.9 to 65 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.26 |