R05240 alloy belongs to the otherwise unclassified metals classification, while AWS ERNiMo-3 belongs to the nickel alloys. There are 14 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is AWS ERNiMo-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
220
Poisson's Ratio 0.36
0.3
Shear Modulus, GPa 57
83
Tensile Strength: Ultimate (UTS), MPa 270
770

Thermal Properties

Latent Heat of Fusion, J/g 210
320
Specific Heat Capacity, J/kg-K 190
400
Thermal Expansion, µm/m-K 6.8
11

Otherwise Unclassified Properties

Density, g/cm3 14
9.1
Embodied Water, L/kg 460
270

Common Calculations

Stiffness to Weight: Axial, points 6.3
13
Stiffness to Weight: Bending, points 13
22
Strength to Weight: Axial, points 5.4
24
Strength to Weight: Bending, points 6.8
21
Thermal Shock Resistance, points 18
24

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.12
Chromium (Cr), % 0
4.0 to 6.0
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
4.0 to 7.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0 to 0.020
23 to 26
Nickel (Ni), % 0 to 0.010
53.7 to 69
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0 to 1.0
Vanadium (V), % 0
0 to 0.6
Residuals, % 0
0 to 0.5