R05240 alloy belongs to the otherwise unclassified metals classification, while EN 1.0446 cast steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is EN 1.0446 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
190
Elongation at Break, % 25
25
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 57
73
Tensile Strength: Ultimate (UTS), MPa 270
530
Tensile Strength: Yield (Proof), MPa 170
270

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Specific Heat Capacity, J/kg-K 190
470
Thermal Expansion, µm/m-K 6.8
12

Otherwise Unclassified Properties

Density, g/cm3 14
7.9
Embodied Water, L/kg 460
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
110
Resilience: Unit (Modulus of Resilience), kJ/m3 90
190
Stiffness to Weight: Axial, points 6.3
13
Stiffness to Weight: Bending, points 13
24
Strength to Weight: Axial, points 5.4
19
Strength to Weight: Bending, points 6.8
18
Thermal Shock Resistance, points 18
17

Alloy Composition

Carbon (C), % 0 to 0.010
0
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
99.935 to 100
Molybdenum (Mo), % 0 to 0.020
0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.0050
0
Sulfur (S), % 0
0 to 0.030
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0