R05240 alloy belongs to the otherwise unclassified metals classification, while EN 1.4421 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is EN 1.4421 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
200
Elongation at Break, % 25
11 to 17
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 57
77
Tensile Strength: Ultimate (UTS), MPa 270
880 to 1100
Tensile Strength: Yield (Proof), MPa 170
620 to 950

Thermal Properties

Latent Heat of Fusion, J/g 210
280
Specific Heat Capacity, J/kg-K 190
480
Thermal Expansion, µm/m-K 6.8
10

Otherwise Unclassified Properties

Density, g/cm3 14
7.8
Embodied Water, L/kg 460
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 90
960 to 2270
Stiffness to Weight: Axial, points 6.3
14
Stiffness to Weight: Bending, points 13
25
Strength to Weight: Axial, points 5.4
31 to 39
Strength to Weight: Bending, points 6.8
26 to 30
Thermal Shock Resistance, points 18
31 to 39

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.060
Chromium (Cr), % 0
15.5 to 17.5
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
74.4 to 80.5
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0 to 0.020
0 to 0.7
Nickel (Ni), % 0 to 0.010
4.0 to 5.5
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.0050
0 to 0.8
Sulfur (S), % 0
0 to 0.020
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0