R05240 Alloy vs. EN 1.4710 Stainless Steel

R05240 alloy belongs to the otherwise unclassified metals classification, while EN 1.4710 stainless steel belongs to the iron alloys. There are 11 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is EN 1.4710 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
190
Elongation at Break, % 25
20
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 57
74

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Specific Heat Capacity, J/kg-K 190
480
Thermal Expansion, µm/m-K 6.8
9.9

Otherwise Unclassified Properties

Density, g/cm3 14
7.7
Embodied Water, L/kg 460
76

Common Calculations

Stiffness to Weight: Axial, points 6.3
14
Stiffness to Weight: Bending, points 13
25

Alloy Composition

Carbon (C), % 0 to 0.010
0.2 to 0.35
Chromium (Cr), % 0
6.0 to 8.0
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
87.4 to 92.3
Manganese (Mn), % 0
0.5 to 1.0
Molybdenum (Mo), % 0 to 0.020
0 to 0.15
Nickel (Ni), % 0 to 0.010
0 to 0.5
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.0050
1.0 to 2.5
Sulfur (S), % 0
0 to 0.030
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0