R05240 Alloy vs. C31600 Bronze
R05240 alloy belongs to the otherwise unclassified metals classification, while C31600 bronze belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R05240 alloy and the bottom bar is C31600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 110 |
| Elongation at Break, % | 25 | |
| 6.7 to 28 |
| Poisson's Ratio | 0.36 | |
| 0.33 |
| Shear Modulus, GPa | 57 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 270 to 460 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 80 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 200 |
| Specific Heat Capacity, J/kg-K | 190 | |
| 380 |
| Thermal Expansion, µm/m-K | 6.8 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 14 | |
| 8.8 |
| Embodied Water, L/kg | 460 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 30 to 58 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 | |
| 28 to 690 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 13 | |
| 18 |
| Strength to Weight: Axial, points | 5.4 | |
| 8.5 to 15 |
| Strength to Weight: Bending, points | 6.8 | |
| 11 to 15 |
| Thermal Shock Resistance, points | 18 | |
| 9.4 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 87.5 to 90.5 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 1.3 to 2.5 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0.7 to 1.2 |
| Niobium (Nb), % | 35 to 42 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.040 to 0.1 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 57.9 to 65 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 5.2 to 10.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |