R05240 Alloy vs. S35500 Stainless Steel
R05240 alloy belongs to the otherwise unclassified metals classification, while S35500 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is R05240 alloy and the bottom bar is S35500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 200 |
| Elongation at Break, % | 25 | |
| 14 |
| Poisson's Ratio | 0.36 | |
| 0.28 |
| Shear Modulus, GPa | 57 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 1330 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 1200 to 1280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 190 | |
| 470 |
| Thermal Expansion, µm/m-K | 6.8 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 14 | |
| 7.8 |
| Embodied Water, L/kg | 460 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 | |
| 180 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 | |
| 3610 to 4100 |
| Stiffness to Weight: Axial, points | 6.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 13 | |
| 25 |
| Strength to Weight: Axial, points | 5.4 | |
| 47 to 53 |
| Strength to Weight: Bending, points | 6.8 | |
| 34 to 37 |
| Thermal Shock Resistance, points | 18 | |
| 44 to 49 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0 | |
| 15 to 16 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 73.2 to 77.7 |
| Manganese (Mn), % | 0 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 0 to 0.010 | |
| 4.0 to 5.0 |
| Niobium (Nb), % | 35 to 42 | |
| 0.1 to 0.5 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0.070 to 0.13 |
| Oxygen (O), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 57.9 to 65 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |