R05252 Alloy vs. C79200 Nickel Silver
R05252 alloy belongs to the otherwise unclassified metals classification, while C79200 nickel silver belongs to the copper alloys. There are 14 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is R05252 alloy and the bottom bar is C79200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 480 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 390 |
| Thermal Expansion, µm/m-K | 6.7 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.4 |
| Embodied Water, L/kg | 600 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.5 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 12 | |
| 19 |
| Strength to Weight: Axial, points | 5.2 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 6.1 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 17 | |
| 16 to 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 59 to 66.5 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0.8 to 1.4 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 11 to 13 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 88.8 to 91 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 9.0 to 11 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 17.9 to 29.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |