R05400 Tantalum vs. 85-platinum 15-iridium
Both R05400 tantalum and 85-platinum 15-iridium are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R05400 tantalum and the bottom bar is 85-platinum 15-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 1.1 to 28 | |
| 5.5 to 34 |
| Poisson's Ratio | 0.34 | |
| 0.38 |
| Shear Modulus, GPa | 69 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 540 | |
| 560 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 130 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 8.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 22 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.2 | |
| 5.7 |
| Stiffness to Weight: Bending, points | 11 | |
| 9.3 |
| Strength to Weight: Axial, points | 3.6 to 9.0 | |
| 7.1 to 9.3 |
| Strength to Weight: Bending, points | 4.8 to 8.8 | |
| 6.9 to 8.3 |
| Thermal Shock Resistance, points | 13 to 32 | |
| 21 to 28 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iridium (Ir), % | 0 | |
| 14.5 to 15.5 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 84.3 to 85.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 99.7 to 100 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |