R05400 Tantalum vs. ASTM B541 Gold
Both R05400 tantalum and ASTM B541 gold are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R05400 tantalum and the bottom bar is ASTM B541 gold.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 1.1 to 28 | |
| 6.0 to 14 |
| Poisson's Ratio | 0.34 | |
| 0.4 |
| Shear Modulus, GPa | 69 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 540 | |
| 670 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 140 to 390 | |
| 480 to 900 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 90 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 170 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 17 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 to 53 | |
| 65 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 50 to 420 | |
| 1090 to 3830 |
| Stiffness to Weight: Axial, points | 6.2 | |
| 3.4 |
| Stiffness to Weight: Bending, points | 11 | |
| 9.0 |
| Strength to Weight: Axial, points | 3.6 to 9.0 | |
| 11 to 19 |
| Strength to Weight: Bending, points | 4.8 to 8.8 | |
| 9.8 to 14 |
| Thermal Shock Resistance, points | 13 to 32 | |
| 36 to 63 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 | |
| 13.5 to 15.5 |
| Gold (Au), % | 0 | |
| 70.5 to 72.5 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 8.0 to 9.0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Silver (Ag), % | 0 | |
| 4.0 to 5.0 |
| Tantalum (Ta), % | 99.7 to 100 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0.7 to 1.3 |
| Residuals, % | 0 | |
| 0 to 0.4 |