R05400 Tantalum vs. Class 2 Tungsten
Both R05400 tantalum and class 2 tungsten are otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is R05400 tantalum and the bottom bar is class 2 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 260 |
| Elongation at Break, % | 1.1 to 28 | |
| 5.7 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 69 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 540 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 140 to 390 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 120 |
| Thermal Conductivity, W/m-K | 59 | |
| 20 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 4.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 15 |
| Embodied Water, L/kg | 650 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 to 53 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 50 to 420 | |
| 640 |
| Stiffness to Weight: Axial, points | 6.2 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 11 | |
| 14 |
| Strength to Weight: Axial, points | 3.6 to 9.0 | |
| 16 |
| Strength to Weight: Bending, points | 4.8 to 8.8 | |
| 13 |
| Thermal Diffusivity, mm2/s | 25 | |
| 11 |
| Thermal Shock Resistance, points | 13 to 32 | |
| 52 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 99.7 to 100 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 92.5 |
| Residuals, % | 0 | |
| 7.5 |