R30001 Cobalt vs. AWS BNi-11
R30001 cobalt belongs to the cobalt alloys classification, while AWS BNi-11 belongs to the nickel alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 18 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R30001 cobalt and the bottom bar is AWS BNi-11.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 86 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 340 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1100 |
| Melting Onset (Solidus), °C | 1260 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 450 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 11 |
| Embodied Energy, MJ/kg | 130 | |
| 160 |
| Embodied Water, L/kg | 460 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 22 | |
| 21 |
| Strength to Weight: Axial, points | 19 | |
| 18 |
| Strength to Weight: Bending, points | 18 | |
| 17 |
| Thermal Shock Resistance, points | 19 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Boron (B), % | 0 | |
| 2.2 to 3.1 |
| Carbon (C), % | 2.0 to 3.0 | |
| 0.3 to 0.5 |
| Chromium (Cr), % | 28 to 32 | |
| 9.0 to 11.8 |
| Cobalt (Co), % | 43 to 59 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 3.0 | |
| 2.5 to 4.0 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 0 to 3.0 | |
| 62.9 to 71.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 to 2.0 | |
| 3.4 to 4.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Tungsten (W), % | 11 to 13 | |
| 11.5 to 12.8 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.5 |