R30003 Cobalt vs. EN 1.6563 Steel

R30003 cobalt belongs to the cobalt alloys classification, while EN 1.6563 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is R30003 cobalt and the bottom bar is EN 1.6563 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 83
73
Tensile Strength: Ultimate (UTS), MPa 970 to 1720
620 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1440
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
45
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 95
3.6
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 8.0
1.7
Embodied Energy, MJ/kg 110
22
Embodied Water, L/kg 400
54

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 32 to 57
22 to 65
Strength to Weight: Bending, points 26 to 38
21 to 43
Thermal Diffusivity, mm2/s 3.3
12
Thermal Shock Resistance, points 26 to 45
18 to 54

Alloy Composition

Boron (B), % 0 to 0.1
0
Carbon (C), % 0 to 0.15
0.38 to 0.44
Chromium (Cr), % 19 to 21
0.7 to 0.9
Cobalt (Co), % 39 to 41
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 10 to 20.5
94.9 to 96.5
Manganese (Mn), % 1.5 to 2.5
0.6 to 0.9
Molybdenum (Mo), % 6.0 to 8.0
0.15 to 0.3
Nickel (Ni), % 14 to 16
1.7 to 2.0
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0 to 1.2
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025