R30003 Cobalt vs. CC752S Brass
R30003 cobalt belongs to the cobalt alloys classification, while CC752S brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is R30003 cobalt and the bottom bar is CC752S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 100 |
| Elongation at Break, % | 10 to 73 | |
| 8.4 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 83 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1720 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 510 to 1090 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 170 |
| Melting Completion (Liquidus), °C | 1400 | |
| 840 |
| Melting Onset (Solidus), °C | 1440 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Conductivity, W/m-K | 13 | |
| 110 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 95 | |
| 24 |
| Density, g/cm3 | 8.4 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 110 | |
| 46 |
| Embodied Water, L/kg | 400 | |
| 330 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 2790 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 32 to 57 | |
| 12 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 13 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 35 |
| Thermal Shock Resistance, points | 26 to 45 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.3 to 0.7 |
| Antimony (Sb), % | 0 | |
| 0 to 0.14 |
| Arsenic (As), % | 0 | |
| 0.040 to 0.14 |
| Boron (B), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 39 to 41 | |
| 0 |
| Copper (Cu), % | 0 | |
| 61.5 to 64.5 |
| Iron (Fe), % | 10 to 20.5 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.2 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 6.0 to 8.0 | |
| 0 |
| Nickel (Ni), % | 14 to 16 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 1.2 | |
| 0 to 0.020 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 | |
| 31.5 to 36.7 |