R30003 Cobalt vs. SAE-AISI 1040 Steel
R30003 cobalt belongs to the cobalt alloys classification, while SAE-AISI 1040 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is R30003 cobalt and the bottom bar is SAE-AISI 1040 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 10 to 73 | |
| 13 to 20 |
| Fatigue Strength, MPa | 320 to 560 | |
| 220 to 340 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1720 | |
| 570 to 640 |
| Tensile Strength: Yield (Proof), MPa | 510 to 1090 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1460 |
| Melting Onset (Solidus), °C | 1440 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 95 | |
| 1.8 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 18 |
| Embodied Water, L/kg | 400 | |
| 46 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 2790 | |
| 270 to 760 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 32 to 57 | |
| 20 to 23 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 19 to 21 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 14 |
| Thermal Shock Resistance, points | 26 to 45 | |
| 18 to 20 |
Alloy Composition
| Boron (B), % | 0 to 0.1 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0.37 to 0.44 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 39 to 41 | |
| 0 |
| Iron (Fe), % | 10 to 20.5 | |
| 98.6 to 99.03 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 6.0 to 8.0 | |
| 0 |
| Nickel (Ni), % | 14 to 16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.2 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |