R30003 Cobalt vs. R30075 Cobalt
Both R30003 cobalt and R30075 cobalt are cobalt alloys. They have 68% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is R30003 cobalt and the bottom bar is R30075 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 to 250 |
| Elongation at Break, % | 10 to 73 | |
| 12 |
| Fatigue Strength, MPa | 320 to 560 | |
| 250 to 840 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 83 | |
| 82 to 98 |
| Tensile Strength: Ultimate (UTS), MPa | 970 to 1720 | |
| 780 to 1280 |
| Tensile Strength: Yield (Proof), MPa | 510 to 1090 | |
| 480 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 320 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1360 |
| Melting Onset (Solidus), °C | 1440 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Conductivity, W/m-K | 13 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.1 |
| Embodied Energy, MJ/kg | 110 | |
| 110 |
| Embodied Water, L/kg | 400 | |
| 530 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 2790 | |
| 560 to 1410 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 to 17 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 32 to 57 | |
| 26 to 42 |
| Strength to Weight: Bending, points | 26 to 38 | |
| 22 to 31 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 3.5 |
| Thermal Shock Resistance, points | 26 to 45 | |
| 21 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Boron (B), % | 0 to 0.1 | |
| 0 to 0.010 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.35 |
| Chromium (Cr), % | 19 to 21 | |
| 27 to 30 |
| Cobalt (Co), % | 39 to 41 | |
| 58.7 to 68 |
| Iron (Fe), % | 10 to 20.5 | |
| 0 to 0.75 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 6.0 to 8.0 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 14 to 16 | |
| 0 to 0.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Tungsten (W), % | 0 | |
| 0 to 0.2 |