R30008 Cobalt vs. ASTM B631 Class B

R30008 cobalt belongs to the cobalt alloys classification, while ASTM B631 class B belongs to the otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is R30008 cobalt and the bottom bar is ASTM B631 class B.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 83
78 to 79

Thermal Properties

Latent Heat of Fusion, J/g 320
150
Melting Completion (Liquidus), °C 1400
2460 to 2480
Specific Heat Capacity, J/kg-K 450
170
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 8.4
14
Embodied Carbon, kg CO2/kg material 8.1
49
Embodied Energy, MJ/kg 110
760

Common Calculations

Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 24
14