R30008 Cobalt vs. ASTM B780 Alloy

R30008 cobalt belongs to the cobalt alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R30008 cobalt and the bottom bar is ASTM B780 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
83
Elongation at Break, % 1.1 to 73
1.1 to 9.1
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 83
30
Tensile Strength: Ultimate (UTS), MPa 950 to 1700
330 to 590

Thermal Properties

Latent Heat of Fusion, J/g 320
140
Specific Heat Capacity, J/kg-K 450
270
Thermal Expansion, µm/m-K 13
18

Otherwise Unclassified Properties

Density, g/cm3 8.4
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.5
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 31 to 56
9.1 to 16
Strength to Weight: Bending, points 25 to 37
11 to 15
Thermal Shock Resistance, points 25 to 44
16 to 29

Alloy Composition

Boron (B), % 0 to 0.0010
0
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 18.5 to 21.5
0
Cobalt (Co), % 39 to 42
0
Copper (Cu), % 0
23.5 to 25.7
Iron (Fe), % 7.6 to 20
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 1.0 to 2.0
0
Molybdenum (Mo), % 6.5 to 7.5
0
Nickel (Ni), % 15 to 18
0.35 to 0.65
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 1.2
0
Silver (Ag), % 0
74 to 76
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 0.060

Comparable Variants