R30012 Cobalt vs. ASTM A182 Grade F911
R30012 cobalt belongs to the cobalt alloys classification, while ASTM A182 grade F911 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R30012 cobalt and the bottom bar is ASTM A182 grade F911.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 1.0 | |
| 20 |
| Fatigue Strength, MPa | 320 | |
| 350 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 86 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 650 | |
| 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 270 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1480 |
| Melting Onset (Solidus), °C | 1280 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 26 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.8 | |
| 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 2.8 |
| Embodied Energy, MJ/kg | 120 | |
| 40 |
| Embodied Water, L/kg | 480 | |
| 90 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.7 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 960 | |
| 650 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 24 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.8 | |
| 6.9 |
| Thermal Shock Resistance, points | 23 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.00030 to 0.0060 |
| Carbon (C), % | 1.4 to 2.0 | |
| 0.090 to 0.13 |
| Chromium (Cr), % | 27 to 32 | |
| 8.5 to 9.5 |
| Cobalt (Co), % | 47.5 to 64.1 | |
| 0 |
| Iron (Fe), % | 0 to 3.0 | |
| 86.2 to 88.9 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 to 1.0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 to 3.0 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.060 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0.040 to 0.090 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 2.0 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 7.5 to 9.5 | |
| 0.9 to 1.1 |
| Vanadium (V), % | 0 | |
| 0.18 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |