R30016 Cobalt vs. CC480K Bronze
R30016 cobalt belongs to the cobalt alloys classification, while CC480K bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is R30016 cobalt and the bottom bar is CC480K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 8.4 | |
| 13 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 85 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 1010 | |
| 300 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 190 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1010 |
| Melting Onset (Solidus), °C | 1270 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 370 |
| Thermal Conductivity, W/m-K | 15 | |
| 63 |
| Thermal Expansion, µm/m-K | 14 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 3.7 |
| Embodied Energy, MJ/kg | 110 | |
| 59 |
| Embodied Water, L/kg | 500 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 72 | |
| 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 33 | |
| 9.6 |
| Strength to Weight: Bending, points | 26 | |
| 11 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 20 |
| Thermal Shock Resistance, points | 24 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0.9 to 1.4 | |
| 0 |
| Chromium (Cr), % | 28 to 32 | |
| 0 |
| Cobalt (Co), % | 49.6 to 66.9 | |
| 0 |
| Copper (Cu), % | 0 | |
| 86 to 90 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0.5 to 2.0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 to 1.5 | |
| 0 |
| Nickel (Ni), % | 0 to 3.0 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0.2 to 2.0 | |
| 0 to 0.020 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 9.0 to 11 |
| Tungsten (W), % | 3.5 to 5.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |