R30075 Cobalt vs. AWS BCo-1
Both R30075 cobalt and AWS BCo-1 are cobalt alloys. They have 70% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R30075 cobalt and the bottom bar is AWS BCo-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 to 250 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 82 to 98 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1280 | |
| 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 420 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1150 |
| Melting Onset (Solidus), °C | 1290 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 8.0 |
| Embodied Energy, MJ/kg | 110 | |
| 110 |
| Embodied Water, L/kg | 530 | |
| 430 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 to 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 42 | |
| 24 |
| Strength to Weight: Bending, points | 22 to 31 | |
| 22 |
| Thermal Shock Resistance, points | 21 to 29 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 to 0.050 |
| Boron (B), % | 0 to 0.010 | |
| 0.7 to 0.9 |
| Carbon (C), % | 0 to 0.35 | |
| 0.35 to 0.45 |
| Chromium (Cr), % | 27 to 30 | |
| 18 to 20 |
| Cobalt (Co), % | 58.7 to 68 | |
| 46 to 54 |
| Iron (Fe), % | 0 to 0.75 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 0.5 | |
| 16 to 18 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 to 1.0 | |
| 7.5 to 8.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.050 |
| Tungsten (W), % | 0 to 0.2 | |
| 3.5 to 4.5 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.5 |