R30075 Cobalt vs. EN 1.4931 Steel

R30075 cobalt belongs to the cobalt alloys classification, while EN 1.4931 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is R30075 cobalt and the bottom bar is EN 1.4931 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210 to 250
200
Elongation at Break, % 12
17
Fatigue Strength, MPa 250 to 840
410
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 82 to 98
76
Tensile Strength: Ultimate (UTS), MPa 780 to 1280
810
Tensile Strength: Yield (Proof), MPa 480 to 840
620

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1290
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
24
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
9.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
11

Otherwise Unclassified Properties

Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 8.1
2.9
Embodied Energy, MJ/kg 110
42
Embodied Water, L/kg 530
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84 to 140
130
Resilience: Unit (Modulus of Resilience), kJ/m3 560 to 1410
970
Stiffness to Weight: Axial, points 14 to 17
14
Stiffness to Weight: Bending, points 24 to 25
25
Strength to Weight: Axial, points 26 to 42
29
Strength to Weight: Bending, points 22 to 31
25
Thermal Diffusivity, mm2/s 3.5
6.5
Thermal Shock Resistance, points 21 to 29
22

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Boron (B), % 0 to 0.010
0
Carbon (C), % 0 to 0.35
0.2 to 0.26
Chromium (Cr), % 27 to 30
11.3 to 12.2
Cobalt (Co), % 58.7 to 68
0
Iron (Fe), % 0 to 0.75
83.2 to 86.8
Manganese (Mn), % 0 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 5.0 to 7.0
1.0 to 1.2
Nickel (Ni), % 0 to 0.5
0 to 1.0
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.1
0
Tungsten (W), % 0 to 0.2
0 to 0.5
Vanadium (V), % 0
0.25 to 0.35