R30075 Cobalt vs. SAE-AISI 1536 Steel
R30075 cobalt belongs to the cobalt alloys classification, while SAE-AISI 1536 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is R30075 cobalt and the bottom bar is SAE-AISI 1536 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 to 250 | |
| 190 |
| Elongation at Break, % | 12 | |
| 14 to 18 |
| Fatigue Strength, MPa | 250 to 840 | |
| 240 to 380 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 20 | |
| 39 to 46 |
| Shear Modulus, GPa | 82 to 98 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1280 | |
| 640 to 720 |
| Tensile Strength: Yield (Proof), MPa | 480 to 840 | |
| 360 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1290 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 8.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 19 |
| Embodied Water, L/kg | 530 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 to 140 | |
| 93 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 to 1410 | |
| 340 to 950 |
| Stiffness to Weight: Axial, points | 14 to 17 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 42 | |
| 23 to 25 |
| Strength to Weight: Bending, points | 22 to 31 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 14 |
| Thermal Shock Resistance, points | 21 to 29 | |
| 20 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.35 | |
| 0.3 to 0.37 |
| Chromium (Cr), % | 27 to 30 | |
| 0 |
| Cobalt (Co), % | 58.7 to 68 | |
| 0 |
| Iron (Fe), % | 0 to 0.75 | |
| 98 to 98.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.2 to 1.5 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Tungsten (W), % | 0 to 0.2 | |
| 0 |