R30075 Cobalt vs. R30001 Cobalt
Both R30075 cobalt and R30001 cobalt are cobalt alloys. They have 81% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R30075 cobalt and the bottom bar is R30001 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 to 250 | |
| 220 |
| Elongation at Break, % | 12 | |
| 1.0 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 82 to 98 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1280 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 310 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1530 |
| Melting Onset (Solidus), °C | 1290 | |
| 1260 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 430 |
| Thermal Conductivity, W/m-K | 13 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 1.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 8.9 |
| Embodied Energy, MJ/kg | 110 | |
| 130 |
| Embodied Water, L/kg | 530 | |
| 460 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 to 17 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 22 |
| Strength to Weight: Axial, points | 26 to 42 | |
| 19 |
| Strength to Weight: Bending, points | 22 to 31 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 3.7 |
| Thermal Shock Resistance, points | 21 to 29 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.35 | |
| 2.0 to 3.0 |
| Chromium (Cr), % | 27 to 30 | |
| 28 to 32 |
| Cobalt (Co), % | 58.7 to 68 | |
| 43 to 59 |
| Iron (Fe), % | 0 to 0.75 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 3.0 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 2.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Tungsten (W), % | 0 to 0.2 | |
| 11 to 13 |