R30155 Cobalt vs. AWS E309L

Both R30155 cobalt and AWS E309L are iron alloys. They have 67% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R30155 cobalt and the bottom bar is AWS E309L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
34
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 81
79
Tensile Strength: Ultimate (UTS), MPa 850
580

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 14
14

Otherwise Unclassified Properties

Base Metal Price, % relative 80
20
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 9.7
3.7
Embodied Energy, MJ/kg 150
52
Embodied Water, L/kg 300
180

Common Calculations

PREN (Pitting Resistance) 37
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 28
21
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 3.2
4.0
Thermal Shock Resistance, points 21
15

Alloy Composition

Carbon (C), % 0.080 to 0.16
0 to 0.040
Chromium (Cr), % 20 to 22.5
22 to 25
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 24.3 to 36.2
55.9 to 65.5
Manganese (Mn), % 1.0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 2.5 to 3.5
0 to 0.75
Nickel (Ni), % 19 to 21
12 to 14
Niobium (Nb), % 0.75 to 1.3
0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tantalum (Ta), % 0.75 to 1.3
0
Tungsten (W), % 2.0 to 3.0
0