R30155 Cobalt vs. EN 1.4931 Steel
Both R30155 cobalt and EN 1.4931 steel are iron alloys. They have 45% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is R30155 cobalt and the bottom bar is EN 1.4931 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 220 | |
240 |
Elastic (Young's, Tensile) Modulus, GPa | 210 | |
200 |
Elongation at Break, % | 34 | |
17 |
Fatigue Strength, MPa | 310 | |
410 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 81 | |
76 |
Tensile Strength: Ultimate (UTS), MPa | 850 | |
810 |
Tensile Strength: Yield (Proof), MPa | 390 | |
620 |
Thermal Properties
Latent Heat of Fusion, J/g | 300 | |
270 |
Maximum Temperature: Mechanical, °C | 1100 | |
600 |
Melting Completion (Liquidus), °C | 1470 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 450 | |
470 |
Thermal Conductivity, W/m-K | 12 | |
24 |
Thermal Expansion, µm/m-K | 14 | |
14 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 80 | |
8.5 |
Density, g/cm3 | 8.5 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 9.7 | |
2.9 |
Embodied Energy, MJ/kg | 150 | |
42 |
Embodied Water, L/kg | 300 | |
100 |
Common Calculations
PREN (Pitting Resistance) | 37 | |
16 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 230 | |
130 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
970 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 23 | |
25 |
Strength to Weight: Axial, points | 28 | |
29 |
Strength to Weight: Bending, points | 24 | |
25 |
Thermal Diffusivity, mm2/s | 3.2 | |
6.5 |
Thermal Shock Resistance, points | 21 | |
22 |
Alloy Composition
Carbon (C), % | 0.080 to 0.16 | |
0.2 to 0.26 |
Chromium (Cr), % | 20 to 22.5 | |
11.3 to 12.2 |
Cobalt (Co), % | 18.5 to 21 | |
0 |
Iron (Fe), % | 24.3 to 36.2 | |
83.2 to 86.8 |
Manganese (Mn), % | 1.0 to 2.0 | |
0.5 to 0.8 |
Molybdenum (Mo), % | 2.5 to 3.5 | |
1.0 to 1.2 |
Nickel (Ni), % | 19 to 21 | |
0 to 1.0 |
Niobium (Nb), % | 0.75 to 1.3 | |
0 |
Nitrogen (N), % | 0 to 0.2 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.030 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.020 |
Tantalum (Ta), % | 0.75 to 1.3 | |
0 |
Tungsten (W), % | 2.0 to 3.0 | |
0 to 0.5 |
Vanadium (V), % | 0 | |
0.25 to 0.35 |