R30155 Cobalt vs. EN 1.8896 Steel
Both R30155 cobalt and EN 1.8896 steel are iron alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is R30155 cobalt and the bottom bar is EN 1.8896 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 34 | |
| 24 |
| Fatigue Strength, MPa | 310 | |
| 280 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 73 |
| Shear Strength, MPa | 570 | |
| 330 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 49 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 2.2 |
| Density, g/cm3 | 8.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.7 | |
| 1.6 |
| Embodied Energy, MJ/kg | 150 | |
| 21 |
| Embodied Water, L/kg | 300 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 230 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 18 |
| Strength to Weight: Bending, points | 24 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 13 |
| Thermal Shock Resistance, points | 21 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0.080 to 0.16 | |
| 0 to 0.14 |
| Chromium (Cr), % | 20 to 22.5 | |
| 0 |
| Cobalt (Co), % | 18.5 to 21 | |
| 0 |
| Iron (Fe), % | 24.3 to 36.2 | |
| 97 to 99.98 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 to 0.2 |
| Nickel (Ni), % | 19 to 21 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 to 0.050 |
| Nitrogen (N), % | 0 to 0.2 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0.75 to 1.3 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |