R30556 Alloy vs. ASTM Grade HP Steel
Both R30556 alloy and ASTM grade HP steel are iron alloys. They have 74% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is R30556 alloy and the bottom bar is ASTM grade HP steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 45 | |
| 5.1 |
| Fatigue Strength, MPa | 320 | |
| 130 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 81 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 350 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 320 |
| Maximum Temperature: Corrosion, °C | 450 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1370 |
| Melting Onset (Solidus), °C | 1330 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 12 |
| Thermal Expansion, µm/m-K | 15 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 34 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 5.8 |
| Embodied Energy, MJ/kg | 130 | |
| 82 |
| Embodied Water, L/kg | 300 | |
| 220 |
Common Calculations
| PREN (Pitting Resistance) | 40 | |
| 27 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 290 | |
| 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 | |
| 170 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 26 | |
| 17 |
| Strength to Weight: Bending, points | 22 | |
| 17 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 3.2 |
| Thermal Shock Resistance, points | 18 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0.1 to 0.5 | |
| 0 |
| Boron (B), % | 0 to 0.020 | |
| 0 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0.35 to 0.75 |
| Chromium (Cr), % | 21 to 23 | |
| 24 to 28 |
| Cobalt (Co), % | 16 to 21 | |
| 0 |
| Iron (Fe), % | 20.4 to 38.2 | |
| 29.2 to 42.7 |
| Lanthanum (La), % | 0.0050 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0.5 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.5 to 4.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 19 to 22.5 | |
| 33 to 37 |
| Niobium (Nb), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0 to 2.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.040 |
| Tantalum (Ta), % | 0.3 to 1.3 | |
| 0 |
| Tungsten (W), % | 2.0 to 3.5 | |
| 0 |
| Zinc (Zn), % | 0.0010 to 0.1 | |
| 0 |