R30816 Cobalt vs. 50Cr-50Ni-Cb Alloy
R30816 cobalt belongs to the cobalt alloys classification, while 50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals. They have 43% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is 50Cr-50Ni-Cb alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Elongation at Break, % | 23 | |
| 5.6 |
| Poisson's Ratio | 0.3 | |
| 0.26 |
| Shear Modulus, GPa | 81 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 9.2 |
| Embodied Energy, MJ/kg | 320 | |
| 130 |
| Embodied Water, L/kg | 440 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 30 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 31 | |
| 21 |
| Strength to Weight: Bending, points | 25 | |
| 20 |
| Thermal Shock Resistance, points | 28 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.25 |
| Carbon (C), % | 0.32 to 0.42 | |
| 0 to 0.1 |
| Chromium (Cr), % | 19 to 21 | |
| 47 to 52 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Iron (Fe), % | 0 to 5.0 | |
| 0 to 1.0 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 43.3 to 51.6 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 1.4 to 1.7 |
| Nitrogen (N), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.5 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |