R30816 Cobalt vs. AISI W1 Steel
R30816 cobalt belongs to the cobalt alloys classification, while AISI W1 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is AISI W1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 590 to 2320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1450 |
| Melting Onset (Solidus), °C | 1460 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 48 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 1.6 |
| Embodied Energy, MJ/kg | 320 | |
| 21 |
| Embodied Water, L/kg | 440 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 21 to 83 |
| Strength to Weight: Bending, points | 25 | |
| 20 to 50 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 13 |
| Thermal Shock Resistance, points | 28 | |
| 22 to 85 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.42 | |
| 0.7 to 1.5 |
| Chromium (Cr), % | 19 to 21 | |
| 0 to 0.15 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 5.0 | |
| 96.4 to 98.9 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.35 to 0.73 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 19 to 21 | |
| 0 to 0.2 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |