R30816 Cobalt vs. EN AC-43400 Aluminum
R30816 cobalt belongs to the cobalt alloys classification, while EN AC-43400 aluminum belongs to the aluminum alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is EN AC-43400 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 280 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 72 |
| Elongation at Break, % | 23 | |
| 1.1 |
| Fatigue Strength, MPa | 250 | |
| 110 |
| Poisson's Ratio | 0.3 | |
| 0.33 |
| Shear Modulus, GPa | 81 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 540 |
| Melting Completion (Liquidus), °C | 1540 | |
| 600 |
| Melting Onset (Solidus), °C | 1460 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 900 |
| Thermal Conductivity, W/m-K | 13 | |
| 140 |
| Thermal Expansion, µm/m-K | 12 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 7.8 |
| Embodied Energy, MJ/kg | 320 | |
| 150 |
| Embodied Water, L/kg | 440 | |
| 1070 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 2.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 22 | |
| 54 |
| Strength to Weight: Axial, points | 31 | |
| 29 |
| Strength to Weight: Bending, points | 25 | |
| 36 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 59 |
| Thermal Shock Resistance, points | 28 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 86 to 90.8 |
| Carbon (C), % | 0.32 to 0.42 | |
| 0 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 5.0 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 | |
| 0.2 to 0.5 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 to 0.55 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 0 to 0.15 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 9.0 to 11 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |