R30816 Cobalt vs. C19020 Copper
R30816 cobalt belongs to the cobalt alloys classification, while C19020 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is C19020 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 120 |
| Elongation at Break, % | 23 | |
| 2.3 to 5.7 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 81 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 440 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 210 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1090 |
| Melting Onset (Solidus), °C | 1460 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 390 |
| Thermal Conductivity, W/m-K | 13 | |
| 190 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 2.8 |
| Embodied Energy, MJ/kg | 320 | |
| 44 |
| Embodied Water, L/kg | 440 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 18 |
| Strength to Weight: Axial, points | 31 | |
| 14 to 18 |
| Strength to Weight: Bending, points | 25 | |
| 14 to 18 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 55 |
| Thermal Shock Resistance, points | 28 | |
| 16 to 21 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.42 | |
| 0 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Copper (Cu), % | 0 | |
| 95.7 to 99.19 |
| Iron (Fe), % | 0 to 5.0 | |
| 0 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 0.5 to 3.0 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.010 to 0.2 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.3 to 0.9 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |