R31233 Cobalt vs. R30003 Cobalt
Both R31233 cobalt and R30003 cobalt are cobalt alloys. They have 78% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is R31233 cobalt and the bottom bar is R30003 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 210 |
| Elongation at Break, % | 17 | |
| 10 to 73 |
| Fatigue Strength, MPa | 220 | |
| 320 to 560 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 85 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 970 to 1720 |
| Tensile Strength: Yield (Proof), MPa | 420 | |
| 510 to 1090 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 310 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1400 |
| Melting Onset (Solidus), °C | 1330 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 12 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.0 |
| Embodied Energy, MJ/kg | 110 | |
| 110 |
| Embodied Water, L/kg | 480 | |
| 400 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 | |
| 600 to 2790 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 33 | |
| 32 to 57 |
| Strength to Weight: Bending, points | 26 | |
| 26 to 38 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 3.3 |
| Thermal Shock Resistance, points | 25 | |
| 26 to 45 |
Alloy Composition
| Boron (B), % | 0 to 0.015 | |
| 0 to 0.1 |
| Carbon (C), % | 0.020 to 0.1 | |
| 0 to 0.15 |
| Chromium (Cr), % | 23.5 to 27.5 | |
| 19 to 21 |
| Cobalt (Co), % | 44.7 to 63.3 | |
| 39 to 41 |
| Iron (Fe), % | 1.0 to 5.0 | |
| 10 to 20.5 |
| Manganese (Mn), % | 0.1 to 1.5 | |
| 1.5 to 2.5 |
| Molybdenum (Mo), % | 4.0 to 6.0 | |
| 6.0 to 8.0 |
| Nickel (Ni), % | 7.0 to 11 | |
| 14 to 16 |
| Nitrogen (N), % | 0.030 to 0.12 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.050 to 1.0 | |
| 0 to 1.2 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Tungsten (W), % | 1.0 to 3.0 | |
| 0 |