R31233 Cobalt vs. S64512 Stainless Steel
R31233 cobalt belongs to the cobalt alloys classification, while S64512 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is R31233 cobalt and the bottom bar is S64512 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 17 | |
| 17 |
| Fatigue Strength, MPa | 220 | |
| 540 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 85 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 1140 |
| Tensile Strength: Yield (Proof), MPa | 420 | |
| 890 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 270 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 28 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 4.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 3.3 |
| Embodied Energy, MJ/kg | 110 | |
| 47 |
| Embodied Water, L/kg | 480 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 | |
| 2020 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 33 | |
| 40 |
| Strength to Weight: Bending, points | 26 | |
| 31 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 7.5 |
| Thermal Shock Resistance, points | 25 | |
| 42 |
Alloy Composition
| Boron (B), % | 0 to 0.015 | |
| 0 |
| Carbon (C), % | 0.020 to 0.1 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 23.5 to 27.5 | |
| 11 to 12.5 |
| Cobalt (Co), % | 44.7 to 63.3 | |
| 0 |
| Iron (Fe), % | 1.0 to 5.0 | |
| 80.6 to 84.7 |
| Manganese (Mn), % | 0.1 to 1.5 | |
| 0.5 to 0.9 |
| Molybdenum (Mo), % | 4.0 to 6.0 | |
| 1.5 to 2.0 |
| Nickel (Ni), % | 7.0 to 11 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0.030 to 0.12 | |
| 0.010 to 0.050 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.050 to 1.0 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |
| Tungsten (W), % | 1.0 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.4 |