R60706 Alloy vs. AISI 446 Stainless Steel

R60706 alloy belongs to the otherwise unclassified metals classification, while AISI 446 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is AISI 446 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 16
23
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 37
79
Tensile Strength: Ultimate (UTS), MPa 580
570
Tensile Strength: Yield (Proof), MPa 390
300

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Specific Heat Capacity, J/kg-K 270
490
Thermal Conductivity, W/m-K 17
17
Thermal Expansion, µm/m-K 6.3
11

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.7
Embodied Water, L/kg 450
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
110
Resilience: Unit (Modulus of Resilience), kJ/m3 760
230
Stiffness to Weight: Axial, points 8.1
15
Stiffness to Weight: Bending, points 23
26
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 9.5
4.6
Thermal Shock Resistance, points 67
19

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.2
Chromium (Cr), % 0 to 0.2
23 to 27
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
69.2 to 77
Manganese (Mn), % 0
0 to 1.5
Nickel (Ni), % 0
0 to 0.75
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0 to 0.25
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 91 to 98
0