R60706 alloy belongs to the otherwise unclassified metals classification, while AWS E2595 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is AWS E2595.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 16
17
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 37
80
Tensile Strength: Ultimate (UTS), MPa 580
850

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
16
Thermal Expansion, µm/m-K 6.3
14

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
190

Common Calculations

Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 24
30
Strength to Weight: Bending, points 23
25
Thermal Diffusivity, mm2/s 9.5
4.2
Thermal Shock Resistance, points 67
21

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.040
Chromium (Cr), % 0 to 0.2
24 to 27
Copper (Cu), % 0
0.4 to 1.5
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
51.4 to 64.5
Manganese (Mn), % 0
0 to 2.5
Molybdenum (Mo), % 0
2.5 to 4.5
Nickel (Ni), % 0
8.0 to 10.5
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0.2 to 0.3
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.2
Sulfur (S), % 0
0 to 0.025
Tungsten (W), % 0
0.4 to 1.0
Zirconium (Zr), % 91 to 98
0