R60706 alloy belongs to the otherwise unclassified metals classification, while AWS E330H belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is AWS E330H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 16
11
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
76
Tensile Strength: Ultimate (UTS), MPa 580
690

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 6.3
13

Otherwise Unclassified Properties

Density, g/cm3 6.7
8.1
Embodied Water, L/kg 450
180

Common Calculations

Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 9.5
3.2
Thermal Shock Resistance, points 67
19

Alloy Composition

Carbon (C), % 0 to 0.050
0.35 to 0.45
Chromium (Cr), % 0 to 0.2
14 to 17
Copper (Cu), % 0
0 to 0.75
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
40.5 to 51.7
Manganese (Mn), % 0
1.0 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
33 to 37
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zirconium (Zr), % 91 to 98
0