R60706 alloy belongs to the otherwise unclassified metals classification, while EN 1.0434 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is R60706 alloy and the bottom bar is EN 1.0434 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 98 | |
190 |
Elongation at Break, % | 16 | |
12 to 28 |
Poisson's Ratio | 0.34 | |
0.29 |
Shear Modulus, GPa | 37 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 580 | |
390 to 540 |
Tensile Strength: Yield (Proof), MPa | 390 | |
250 to 450 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Specific Heat Capacity, J/kg-K | 270 | |
470 |
Thermal Conductivity, W/m-K | 17 | |
52 |
Thermal Expansion, µm/m-K | 6.3 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 6.7 | |
7.9 |
Embodied Water, L/kg | 450 | |
46 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 | |
39 to 140 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 760 | |
170 to 540 |
Stiffness to Weight: Axial, points | 8.1 | |
13 |
Stiffness to Weight: Bending, points | 23 | |
24 |
Strength to Weight: Axial, points | 24 | |
14 to 19 |
Strength to Weight: Bending, points | 23 | |
15 to 19 |
Thermal Diffusivity, mm2/s | 9.5 | |
14 |
Thermal Shock Resistance, points | 67 | |
12 to 17 |
Alloy Composition
Aluminum (Al), % | 0 | |
0.020 to 0.060 |
Carbon (C), % | 0 to 0.050 | |
0.15 to 0.19 |
Chromium (Cr), % | 0 to 0.2 | |
0 |
Hafnium (Hf), % | 0 to 4.5 | |
0 |
Hydrogen (H), % | 0 to 0.0050 | |
0 |
Iron (Fe), % | 0 to 0.2 | |
98.8 to 99.18 |
Manganese (Mn), % | 0 | |
0.65 to 0.85 |
Niobium (Nb), % | 2.0 to 3.0 | |
0 |
Nitrogen (N), % | 0 to 0.025 | |
0 |
Oxygen (O), % | 0 to 0.16 | |
0 |
Phosphorus (P), % | 0 | |
0 to 0.025 |
Silicon (Si), % | 0 | |
0 to 0.1 |
Sulfur (S), % | 0 | |
0 to 0.025 |
Zirconium (Zr), % | 91 to 98 | |
0 |