R60706 Alloy vs. EN 1.4762 Stainless Steel

R60706 alloy belongs to the otherwise unclassified metals classification, while EN 1.4762 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is EN 1.4762 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
200
Elongation at Break, % 16
13
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 37
78
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 390
310

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Specific Heat Capacity, J/kg-K 270
490
Thermal Conductivity, W/m-K 17
17
Thermal Expansion, µm/m-K 6.3
10

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.6
Embodied Water, L/kg 450
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
67
Resilience: Unit (Modulus of Resilience), kJ/m3 760
250
Stiffness to Weight: Axial, points 8.1
15
Stiffness to Weight: Bending, points 23
26
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 23
21
Thermal Diffusivity, mm2/s 9.5
4.6
Thermal Shock Resistance, points 67
22

Alloy Composition

Aluminum (Al), % 0
1.2 to 1.7
Carbon (C), % 0 to 0.050
0 to 0.12
Chromium (Cr), % 0 to 0.2
23 to 26
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
69.7 to 75.1
Manganese (Mn), % 0
0 to 1.0
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0.7 to 1.4
Sulfur (S), % 0
0 to 0.015
Zirconium (Zr), % 91 to 98
0